1, The repair agent is generally used as the base material, or can be used alone, with the reinforcement band repair, the repair effect is better.
2, The maximum temperature of the repair agent is 120 ºC.
3, It can resist general inorganic acid, organic acid, alcohol, alkali, amine, etc. For example: 10% hydrochloric acid, 10% nitric acid, carbonic acid, 10% hydrobromic acid, 20% nitrite, 5% phosphoric acid, 10% sulfuric acid, 20% ammonia water, lime water, 20% potassium hydroxide, 20% sodium hydroxide, propanol, butanol, ethylene glycol, diethyl hydrogen salt, methylamine (water content 75%), bicarbonate, mineral oil, inorganic salt, etc.
4, Weight: 1000g / 2000g, origin: USA
5, When the load is 1kg, the data are as follows: H10 wheel (wet) 0.13cm3/per thousand revolutions, CS17 wheels (dry) 0.05cm3/per kilo revolution
6, The thermal expansion is 35.5ppm/0c according to ASTM e228
7, According to ASTM d1002, the tensile shear strength (surface sandblasting treatment) is 191kg / cm2 for low carbon steel, 209kg / cm2 for stainless steel, 160kg / cm2 for brass and 156kg / cm2 for copper
8, The compressive strength is tested according to ASTM d695, and the typical value is 916kg / cm2
9, Electrical characteristics: withstand voltage: 1280v / mm (ASTM d149); capacitance: 3.2 (100Hz) (ASTM k1510) 6 (1MHz); power consumption factor < 0.0005 (1MHz) (ASTM D150); body resistance: 1.02 × 1015 Ω. Cm (ASTM D257); surface resistance: 5.76 × 1013 Ω (ASTM D257)
10, According to ASTM d750, the typical value is 704kg / cm2
11, The hardness is tested according to ASTM d785, and the hardness is Rockwell r104
12, The typical value of impact strength of inverted V-groove is 48 J / m
13, Shrinkage 0.0% (min) 0.005% (max)
14, Ratio: weight mixing ratio 5:1, volume ratio 3:1
Storage period: from 0 ºC to 30 ºC, the base material and curing agent shall be stored respectively, and the storage period shall be at least 5 years.
Scope of application: it is used to reconstruct metal repair system damaged by chemical corrosion. It is suitable for repairing centrifuge, turbine pump, butterfly valve, pipeline, fan, propeller, tubesheet, reaction tank / kettle, heat exchanger, pump blade and pump nozzle, transformer, etc
Schedule: operation and curing schedule
2, The maximum temperature of the repair agent is 120 ºC.
3, It can resist general inorganic acid, organic acid, alcohol, alkali, amine, etc. For example: 10% hydrochloric acid, 10% nitric acid, carbonic acid, 10% hydrobromic acid, 20% nitrite, 5% phosphoric acid, 10% sulfuric acid, 20% ammonia water, lime water, 20% potassium hydroxide, 20% sodium hydroxide, propanol, butanol, ethylene glycol, diethyl hydrogen salt, methylamine (water content 75%), bicarbonate, mineral oil, inorganic salt, etc.
4, Weight: 1000g / 2000g, origin: USA
5, When the load is 1kg, the data are as follows: H10 wheel (wet) 0.13cm3/per thousand revolutions, CS17 wheels (dry) 0.05cm3/per kilo revolution
6, The thermal expansion is 35.5ppm/0c according to ASTM e228
7, According to ASTM d1002, the tensile shear strength (surface sandblasting treatment) is 191kg / cm2 for low carbon steel, 209kg / cm2 for stainless steel, 160kg / cm2 for brass and 156kg / cm2 for copper
8, The compressive strength is tested according to ASTM d695, and the typical value is 916kg / cm2
9, Electrical characteristics: withstand voltage: 1280v / mm (ASTM d149); capacitance: 3.2 (100Hz) (ASTM k1510) 6 (1MHz); power consumption factor < 0.0005 (1MHz) (ASTM D150); body resistance: 1.02 × 1015 Ω. Cm (ASTM D257); surface resistance: 5.76 × 1013 Ω (ASTM D257)
10, According to ASTM d750, the typical value is 704kg / cm2
11, The hardness is tested according to ASTM d785, and the hardness is Rockwell r104
12, The typical value of impact strength of inverted V-groove is 48 J / m
13, Shrinkage 0.0% (min) 0.005% (max)
14, Ratio: weight mixing ratio 5:1, volume ratio 3:1
Storage period: from 0 ºC to 30 ºC, the base material and curing agent shall be stored respectively, and the storage period shall be at least 5 years.
Scope of application: it is used to reconstruct metal repair system damaged by chemical corrosion. It is suitable for repairing centrifuge, turbine pump, butterfly valve, pipeline, fan, propeller, tubesheet, reaction tank / kettle, heat exchanger, pump blade and pump nozzle, transformer, etc
Schedule: operation and curing schedule